P2000 / 1.4452
Jérôme Evrard
Sales Manager
+41 (0)44 823 88 26
Chemical composition of 1.4452
| C | ≤ 0.15 |
|---|---|
| Mn | 12.0-16.0 |
| Cr | 16.0-20.0 |
| N | 0.75-1.00 |
| Mo | 2.5-4.2 |
| Nb | ≤ 0.25 |
| Fe | rest |
| Ni | nickel free |
Mechanical properties of Alloy P2000
| Property | Value |
|---|---|
| Solution heat treated | Typical values |
| Tensile strength Rm | 980-1120 MPa |
| Yield strength Rp 0.2 | 610-720 MPa |
| Elongation after fracture | 55-65% |
| Reduction of area A | 65-75% |
| Cold worked precipitation hardened | Typical values |
| Tensile strength Rm | Over 2000 MPa possible |
Delivery program
| Dimensions (Ø) mm | For samples only |
|---|---|
| 0.8 | ● |
| 1.02 | ● |
| 1.30 | ● |